王浩,丁怀伟,温梦,佟伟
WANG Hao1,DING Huai-wei2,WEN Meng1,TONG Wei3(1.College of Pharmaceutical Science

• 1:辽宁医学院药学院
• 2:沈阳药科大学制药工程学院
• 3:辽宁医学院基础医学院

摘要(Abstract)：

目的用油包水乳液静电纺丝法制备并评价包载有L-肉毒碱的聚乙二醇-b-聚ε-己内酯电纺纤维毡。方法将L-肉毒碱溶解在水中为水相,将聚乙二醇与聚ε-己内酯嵌段质量比为1∶75的共聚物和1∶5的共聚物溶解在二氯甲烷中为油相,混合并超声形成W/O乳液后静电纺丝得纤维毡。扫描电子显微镜观察纤维毡形态并用图形软件进行纤维直径分布分析,广角X-射线衍射扫描观察纤维表面结晶状态,差示扫描量热评价药物在高分子材料中的结合状态,高效液相色谱测定药物体外释放结果。结果随着油相中聚乙二醇与聚酯嵌段质量比为1∶75和1∶5两种共聚物的含量比例由高到低,纤维形状由直径较均匀的纤维向直径不均匀的纤维转变,最终形成连接珠形态,平均直径和最大直径逐渐增高。所得纤维表面光滑无结晶态物质析出,X-射线衍射没有发现L-肉毒碱特征峰出现。差示扫描量热结果显示L-肉毒碱的加入使纤维的玻璃化温度降低。随着平均直径的增高,L-肉毒碱释放速率逐渐减慢。结论采用较高相对分子质量聚酯作为成纤材料,相对分子质量较低且聚乙二醇嵌段比例较高的嵌段聚酯为乳化剂,可制得载L-肉毒碱纤维毡作为局部药物控制释放系统。
Objective To prepare and evaluate L-carnitine entrapped polyethylene glycol blocked polyε-caprolactone electrospun fibrous mats by aqueous in oil emulsion method.Methods L-carnitine was dissolved in water which used as inner aqueous phase,and polyethylene glycol blocked polyε-caprolactone with 1∶ 75 and 1∶ 5 of polyethylene and polyε-caprolactone block ratio was dissolved in dichloromethane which was used as outer oil phase.These two phases were mixed and ultra-sonicated to form W/O emulsion before electrospinning to obtain fibrous mats which were observed morphologically by scanning electron microscope.Fiber surface crystalline state was detected by wide angle X-ray diffraction.L-carnitine-polymer material composition state was evaluated by differential scanning calorimetry.High performance liquid chromatography was used to determine drug in vitro release.Results Surfaces of fibers were smooth and as the ratio of polyethylene glycol blocked polyester with blocks of 1∶ 75 and 1∶ 5 in the oil phase changed,shape of fibers changed from homogeneous-diameter fiber to unhomogeneous ones,and at last to the morphology of beads linked by fibers.Wide angle X-ray diffraction indicated no character peak of L-carnitine.Differential scanning calorimetry presented that addition of L-carnitine lowered the glass temperature of the fibrous mats.As the average diameter became higher,release speed of L-carnitine became lower.Conclusions By using respectively high and low molecule weight polyester as fiber-formation material and emulsifier in which the later contains high ratio of polyethylene glycol block,L-carnitine fibrous mats can be prepared for local drug delivery system.

关键词(KeyWords)： 纤维;L-肉毒碱;静电纺丝;W/O乳液;聚ε-己内酯;聚乙二醇
fiber;L-carnitine;electrospinning;W/O emulsion;polyε-caprolactone;polyethylene glycol

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 王浩,丁怀伟,温梦,佟伟
WANG Hao1,DING Huai-wei2,WEN Meng1,TONG Wei3(1.College of Pharmaceutical Science

DOI: 10.14066/j.cnki.cn21-1349/r.2013.01.006

参考文献(References)：

• [1]沈同,王镜岩,赵邦悌,等.生物化学:下册[M].2版.北京:高等教育出版社,1991:153-154.
• [2]洪卫国,杨明.L-肉碱的生物学作用[J].国外医学:生理病理科学与临床分册,1997,17(4):356-359.
• [3]李克,李伟,黄宇烽,等.精浆游离L-肉毒碱水平及其与精子密度、活动率及活力相关性的研究[J].中华男科学杂志,2007,13(2):143-146.
• [4]VICARI E,CALOGERO A E.Effects of treatment withcarnitines in infertile patients with prostato-vesiculo-ep-ididymitis[J].Human Reproduction,2001,16(11):2338-2342.
• [5]陆继伟,裴元英.阴道给药系统的剂型发展[J].中国临床药学杂志,2003,12(2):123-127.
• [6]陈登龙,李敏,房乾.电纺丝技术在纳米结构高分子支架中的应用[J].中国修复重建外科杂志,2007,21(4):411-415.
• [7]KENAWY E R,ABDEL-HAY E,WNEK G E.Process-ing of nanofibers through electrospinning as drug deliv-ery systems[J].Material Chemistry and Physics,2009,113(1):296-302.
• [8]JIANG H,HU Y,LI Y,et al.A facile technique to pre-pare biodegradable coaxial electrospun nanofibers forcontrolled release of bioactive agents[J].Journal ofControlled Release,2005,108(2/3):237-243.
• [9]SARAF A,BAGGETT L S,PAPHAEL R M,et al.Reg-ulated non-viral gene delivery from coaxial electrospunfiber mesh scaffolds[J].Journal of Controlled Release,2010,143(1):95-103.
• [10]XU Xiu-ling,CHEN Xue-si,MA Ping-an,et al.The re-lease behavior of doxorubicin hydrochloride from medi-cated fibers prepared by emulsion-electrospinning[J].European Journal of Pharmaceutics and Biopharmaceu-tics,2008,70(1):165-170.
• [11]王浩,宋宏锐,邓英杰,等.聚α-羟基辛酸对W/O乳液电纺聚乳酸纤维毡中阿霉素释放的影响[J].合成化学,2010,18(3):273-279.
• [12]XU Xiu-ling,YANG Li-xin,XU Xiao-yi,et al.Ultrafinemedicated fibers electrospun from W/O emulsions[J].Journal of Controlled Release,2005,108(1):33-42.
• [13]ZENG Jing,XU Xiu-ling,CHEN Xue-si,et al.Biode-gradable electrospun fibers for drug delivery[J].Jour-nal of Controlled Release,2003,92(3):227-231.
• [14]梁文平.乳状液科学与技术基础[M].北京:科学出版社,2001.
• [15]杨安乐,孙康,吴人洁.聚ε-己内酯的合成、改性和应用进展[J].高分子通报,2000(2):52-57.
• [16]赵三平,尹玥,冯增国.PCL-PEG-PCL嵌段共聚物的合成与性能[J].功能高分子学报,2002,14(1):67-71.
• [17]WANG C,CHIEN H S,YAN K W,et al.Correlationbetween processing parameters and microstructure ofelectrospun poly(D,L-lactic acid)nanofibers[J].Poly-mer,2009,50(25):6100-6110.
• [18]MARETSCHEK S,GREINER A,KISSEL T.Electro-spun biodegradable nanofiber nonwowens for controlledrelease of proteins[J].Journal of controlled Release,2008,127(2):180-187.
• [19]TEMENOFF J S,MIKOS A G.生物材料——生物学与材料科学的交叉[M].王远亮译.北京:科学出版社,2009.
• [20]邵秀芬,严琳,汪江山,等.离子对RP-HPLC法测定左卡尼汀片剂的含量[J].药学进展,2004,28(3):131-134.
• [21]崔福德.药剂学[M].7版.北京:人民卫生出版社,2011:422-426.
• [22]TAEPAIBOON P,RUNGSARDTHONG U,SUPAPHOLP.Drug-loaded electrospun mats of poly(vinyl alcohol)fibres and their release characteristics of four modeldrugs[J].Nanotechnology,2006,17(9):2317-2329.
• [23]IGNATIOUS F,SUN L,LEE C P,et al.Electrospunnanofibers in oral drug delivery[J].PharmaceuticalResearch,2010,27(4):576-588.
• [24]王浩,邓英杰,焦自学,等.聚L-乳酸与聚乙二醇-b-聚L-乳酸电纺纤维中布洛芬的释放[J].沈阳药科大学学报,2010,27(9):686-694.
• [25]仉文升,李安良.药物化学[M].北京:高等教育出版社,1999:323-324.